A691 CM70 CLASS21 TIUB
A691 Karbon dan Paip Keluli Aloi, Dikimpal Gabungan Elektrik untuk Perkhidmatan Tekanan Tinggi pada Suhu Tinggi
Hantar pertanyaan
Berbual sekarang
pengenalan produk
| JADUAL 1 Bahan Pinggan | ||||
| Gred Paip | Jenis Keluli | Spesifikasi ASTM | HB, maks A | |
| Nombor | Gred | |||
| CM{0}} | keluli karbon-molibdenum | A204/A204M | A | 201 |
| CM{0}} | keluli karbon-molibdenum | A204/A204M | B | 201 |
| CM{0}} | keluli karbon-molibdenum | A204/A204M | C | 201 |
| CMSH-70 | keluli karbon-mangan-silikon, dinormalkan | A537/A537M | 1 | |
| CMS-75 | keluli karbon-mangan-silikon | A299/A299M | . . . | . . . |
| CMSH-80 | keluli karbon-mangan-silikon, dipadamkan dan dibaja | A537/A537M | 2 | |
| 1 ⁄ 2 CR | 1 ⁄ 2 % kromium, 1 ⁄ 2 % keluli molibdenum | A387/A387M | 2 | 201 |
| 1CR | 1 % kromium, 1 ⁄ 2 % keluli molibdenum | A387/A387M | 12 | 201 |
| 1 1 ⁄ 4 CR | 1 1 ⁄ 4 % kromium, 1 ⁄ 2 % keluli molibdenum | A387/A387M | 11 | 201 |
| 2 1 ⁄ 4 CR | 2 1 ⁄ 4 % kromium, 1 % keluli molibdenum | A387/A387M | 22 | 201 |
| 3CR | 3 % kromium, 1 % keluli molibdenum | A387/A387M | 21 | 201 |
| 5CR | 5 % kromium, 1 ⁄ 2 % keluli molibdenum | A387/A387M | 5 | 225 |
| 9CR | 9 % kromium, 1 % keluli molibdenum | A387/A387M | 9 | 241 |
| 91 | 9 % kromium, 1 % molibdenum, vanadium, niobium C | A387/A387M | 91 B | 241 |
| JADUAL 2 Parameter Rawatan Haba A | |||||
| Gred Paip | ASTM Spesifikasi |
Rawatan Haba Selepas Kimpalan Julat Suhu (Menghilangkan Tekanan), darjah F (darjah) |
Menormalkan suhu, maks melainkan dinyatakan sebaliknya, darjah F ( darjah ) |
Pelindapkejutan suhu, maks melainkan dinyatakan sebaliknya, darjah F ( darjah ) |
Suhu Pembajaan, 分钟, darjah F( darjah ) |
| CM{0}} | A204/A204M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CM{0}} | A204/A204M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CM{0}} | A204/A204M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CMSH-70 | A537/A537M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CMS-75 | A299/A299M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CMSH-80 | A537/A537M | 1100 至 1200 [590 至 650] | 乙 | 1700 [925] | 1100 至 1250 [590 至 675] |
| 1 ⁄ 2 CR | A387/A387M | 1100 至 1300 [590 至 705] | 1850 [1010] | 1700 [925] | 1150 至 1375 [620 至 745] |
| 1CR | A387/A387M | 1100 至 1350 [590 至 730] | 1850 [1010] | 1700 [925] | 1150 至 1375 [620 至 745] |
| 11⁄4 CR | A387/A387M | 1100 至 1375 [590 至 745] | 1850 [1010] | 1700 [925] | 1150 至 1375 [620 至 745] |
| 21 ⁄ 4 CR | A387/A387M | 1200 至 1400 [650 至 760] | 1850 [1010] | 1700 [925] | 1250 至 1400 [675 至 760] |
| 3CR | A387/A387M | 1200 至 1400 [650 至 760] | 1850 [1010] | 1700 [925] | 1250 至 1400 [675 至 760] |
| 5CR | A387/A387M | 1200 至 1400 [650 至 760] | 1850 [1010] | 1650 [900] | 1300 至 1400 [705 至 760] |
| 9CR | A387/A387M | 1325 至 1375 [715 至 745] | C | . . . | 1325 至 1375 [715 至 745] |
| 91 | A387/A387M | 1350 至 1420 [730 至 770] | 1900 至 2000 [1040 至 1095] | 1900分钟[1040分钟] | 1350 至 1440 [730 至 780] |
| 类别名称如下 | |||
| 班级 | 管材热处理 | 射线照相, 参见章节 |
压力测试, 参见章节 |
| 10 | 没有任何 | 没有任何 | 没有任何 |
| 11 | 没有任何 | 9 | 没有任何 |
| 12 | 没有任何 | 9 | 8.3 |
| 13 | 没有任何 | 没有任何 | 8.3 |
| 20 | 应力消除,见5.3.1 | 没有任何 | 没有任何 |
| 21 | 应力消除,见5.3.1 | 9 | 没有任何 |
| 22 | 应力消除,见5.3.1 | 9 | 8.3 |
| 23 | 应力消除,见5.3.1 | 没有任何 | 8.3 |
| 30 | 归一化,见 5.3.2 | 没有任何 | 没有任何 |
| 31 | 归一化,见 5.3.2 | 9 | 没有任何 |
| 32 | 归一化,见 5.3.2 | 9 | 8.3 |
| 33 | 归一化,见 5.3.2 | 没有任何 | 8.3 |
| 40 | 正火和回火,见 5.3.3 | 没有任何 | 没有任何 |
| 41 | 正火和回火,见 5.3.3 | 9 | 没有任何 |
| 42 | 正火和回火,见 5.3.3 | 9 | 8.3 |
| 43 | 正火和回火,见 5.3.3 | 没有任何 | 8.3 |
| 50 | 淬火和回火,见5.3.4 | 没有任何 | 没有任何 |
| 51 | 淬火和回火,见5.3.4 | 9 | 没有任何 |
| 52 | 淬火和回火,见5.3.4 | 9 | 8.3 |
| 53 | 淬火和回火,见5.3.4 | 没有任何 | 8.3 |
Cool tags: A691 CM70 CLASS21 TUBE, China A691 CM70 CLASS21 TUBE pengilang, pembekal, ASTM A672 Gred B60 C65 EFW Pipe Steel, အကျိုးခံစားခွင့်ပါဝါဆ weldrofused pipe, Paip EFW, Paip keluli karbon Erw, LSAW PIPES, ဂဟေဆော်ဂျီဆ Weldrofused ပိုက်